Tensile strength of a material is the tension stress at which a material breaks or permanently deforms (changes shape) Toughness, Resilience, Poisson’s ratio can also be found by the use of this testing technique. This data is plotted as load vs elongation and then converted to engineering stress (load/original area) vs engineering strain (fractional change in length over the test section assuming the deformation is uniform)

Procedure of Strength Test:

A standard test piece (gauge length 8ft) is gripped at both ends in the jaws of UTM - Universal Testing Machine which slowly exerts an axial pull so that the steel is stretched until it breaks. The major parameters that describe the stress-strain curve obtained during the tension test are the:

1. Ultimate tensile strength (UTS)
2. Yield strength or yield point (sy)
3. Elastic modulus (E)
4. Percent elongation (?L%) and
5. The reduction in area (RA%).

Toughness, Resilience, Poisson’s ratio can also be found by the use of this testing technique. This data is plotted as load vs elongation and then converted to engineering stress (load/original area) vs engineering strain (fractional change in length over the test section assuming the deformation is uniform.

Engineering Stress:

Stress s = P/Ao ( Load/Initial cross-sectional area)

Strain =  e = ?l/lo (Elongation/Initial gauge length)

Engineering stress and strain are independent of the geometry of the specimen.

If the true cross section is measured during the test the True Stress and True Strain may be calculated. Tensile tests are commonly performed on substances such as metals, plastics, wood, and ceramics.

Units of Measurement:

Tensile testing systems use a number of different units of measurement. The International System of Units, or SI, recommends the use of either Pascals (Pa) or Newtons per square meter (N/m²) for describing tensile strength. In the United States, many engineers measure tensile strength in kilo-pound per square inch (KSI).

Related Articles to this Article

True Stress & True Strain | Engineering Stress-Strain

The true stress (ø) uses the instantaneous or actual area of the specimen at any given point, as op

UTM - Universal Testing Machine

A machine used to test specimens for tensile strength, compressive strength, shear strength and to

Engineering Stress and Strain - Curve

These quantities are defined relative to the original area and length of the specimen. The engineeri

Stability - Stable & Unstable Structures & Members

The resistance offered by a structure to undesirable movement like sliding, collapsing and over tu

Plastic Analysis

Plastic analysis is defined as the analysis in which the criterion for the design of structures is

Read more similar Articles